High-temperature Protection of a Titanium-carbide Ceramal with a Ceramic-metal Coating Having a High Chromium Content

Dwight G. Moore, Stanley G. Benner, William N. Harrison — 1951

At a blade temperature of 1800 degrees F, this coating would probably greatly prolong the life of a K-138 turbine blade under operating conditions sufficiently severe to accelerate failure of the uncoated blade by oxidation.